Kromium corundum opeka refers to a refractory product made of corundum containing Cr ₂ O3, with the main mineral composition being α - Al ₂ O3- Cr ₂ O3 solid solution, and minor minerals containing a small amount of composite spinel or chromium oxide. It utilizes the characteristic of forming a continuous solid solution between Cr ₂ O3 and Al ₂ O3, and has higher high-temperature performance than pure corundum products. The conventional Cr ₂ O3 content is 9% -15%. Bricks used in the petrochemical industry need to meet the requirements of low silicon, low iron, low alkali, and high purity. This product is divided into two categories: cast and sintered, usually referring to sintered type. Prepare using α - Al ₂ O3 as the main material, add chromium oxide powder, mix and shape it, and then high-temperature burn it, or use grouting method to make the billet. The product has a room temperature compressive strength of>150MPA in obsežna gostota večje ali enaka 3,0 g/cm ³ in se lahko upira koroziji zaradi metalurške žlindre in taline stekla. V glavnem se uporablja za obloge steklenih peči, podporne peči za uplinjanje, ne - železove talilne peči in prepustne opeke za jeklene legice
1. Uvod:
Chrome Corundum opekase nanaša na korundske ognjevzdržne izdelke, ki vsebujejo CR2O3. Pri visokih temperaturah CR2O3 in AL2O3 tvorita neprekinjeno trdno raztopino, kar ima za posledico vrhunsko visoko - temperaturno delovanje izdelkov kroma korunduma v primerjavi s čistimi izdelki korunduma. Opeke kroma korunduma, ki se uporabljajo za peči za uplinjanje v petrokemični industriji, morajo biti nizko silicij, nizko železo, nizka alkalija, visoka čistost, poleg tega pa imajo visoko gostoto in moč. Široko uporabljeni izdelki za krom korundum imajo vsebnost CR2O3 večinoma v območju od 9 do 15%
2. Mineralna sestava
Glavna mineralna sestava je - al2o3-cr2o3 trdna raztopina. Sekundarna mineralna sestava je ognjevzdržna opeka z majhno količino sestavljenega spinela (ali brez sestavljenega spinela) in vsebnostjo kroma oksida od 1% do 30%. Obstajata dve vrsti zlivanih opek za krom korundum in sintrane opeke za krom korundum. Na splošno se opečna opeka Chromium corundum nanaša na sintrano opeko chromium corundum
3. Proizvodnjaopečne opeke kroma
Z uporabo - al2O3 kot surovine, dodate ustrezno količino prahu kroma oksida in kroma korundum Clinker finega prahu, oblikovanje in streljanje pri visoki temperaturi. Vsebnost kroma oksida v sintranih opečnih opekah s kromom je na splošno nižja od vsebine opečnih opečnih opek. Alternativno lahko metodo vlivanja gnojevke uporabimo za pripravo debele kaše z enakomerno mešanjem - al2O3 v prahu in kromijevem oksidu v prahu, dodajanju debondonskih sredstev in organskih vezivov ter dodajanju nekaj Chromium Corundum Clinker. Opečno telo je mogoče izdelati z metodo fugiranja in nato izstreliti. Lahko se uporablja kot obloga za steklene peči, pokrije opeke za narisane luknje iz steklenega pretoka in kot podloga za železno pred - naprave za čistilne naprave, sežigalnice za smeti, uplinjače, pod katerim pod pritiskom na premog itd.
4. Aplikacija
Uporabaopečne opeke kromaje postal bolj razširjen. Ena vrsta je opeka iz kroma korunduma, narejene predvsem iz kovinske kromične žlindre, ki se pogosto uporabljajo v električnih pečeh in pečh za taljenje cinka. Kromijeve opeke imajo odlično stabilnost toplotne vibracije in visoko - zmogljivost temperature, poleg tega pa izpolnjujejo zahteve nacionalnega krožnega gospodarstva.
Pri talinju bakra se pogosto uporablja še ena vrsta ognjevzdržne opeke, imenovana aluminijev krom, ki razbija monopol magnezijskih kromijskih opek v enem padcu